干法纺丝制备α-Al_2O_3陶瓷纤维及其力学性能研究Study on Preparation and Mechanical Properties of α-Al_2O_3 Ceramic Fiber by Dry Spinning
李建军;郑顺金;焦秀玲;陈代荣;
摘要(Abstract):
以异丙醇铝和过氧化氢经水热反应制备的拟薄水铝石为原料,合成了可纺性铝溶胶,用干法纺丝法制备了氧化铝凝胶纤维,烧结后得到了α-Al_2O_3连续纤维,对烧结工艺研究表明:慢速升温至650℃后在1300℃下快速烧结10 min后,制备的α-Al_2O_3纤维直径均匀,约10μm,最大断裂强度为1.37 GPa。
关键词(KeyWords): 干法纺丝;α-Al_2O_3;陶瓷纤维
基金项目(Foundation):
作者(Authors): 李建军;郑顺金;焦秀玲;陈代荣;
DOI: 10.16521/j.cnki.issn.1001-9642.2021.04.006
参考文献(References):
- [1]傅绍漯.氧化铝纤维的现状与展望[J].材料导报,1990,2:12-17.
- [2]Tan H B,Ma X L,Fu M X.Preparation of Continuous Alumina Gel Fibres by Aqueous Sol-Gel Process[J].Bull.Mater.Sci.,2013,36(1):153-156.
- [3] Venkatesh R,Ramanan S R.Influence of Processing Variables on the Microstructure of Sol-G el Spun Alumina Fibers[J].Materials Letters,2002,55(3):189-195.
- [4]Sedaghat A,Taheri-Nassaj E,Naghizadeh R.An Alumina Mat with a Nano Microstructure Prepared by Centrifugal Spinning Method[J].J.Non-Cryst.Solids,2006,352(26-27):2818-2828.
- [5]陈代荣,韩伟健,李思维,等.连续陶瓷纤维的制备、结构、性能和应用:研究现状及发展方向[J].现代技术陶瓷,2018,39(3):183-193.
- [6]邵斌.连续陶瓷纤维的制备、应用及研究现状[J].中国粉体工业,2020,3:20-23.
- [7]乔健,刘和义,崔宏亮,等.连续氧化铝纤维的制备及应用[J].中国陶瓷,2015,51(8):1-5.
- [8]崔之开.陶瓷纤维[M].北京:化学工业出版社,2004.
- [9]Bunsell A R,Berger M H.Fine Diameter Ceramic Fibers[J].J.Eur.Ceram.Soc.,2000,20:2249-2260.
- [10]王德刚,仲蕾兰,顾利霞.氧化铝纤维的制备及应用[J].化工新型材料,2002,30(4):17-19.
- [11]Levin I,Brandon D.Metastable Alumina Polymorphs:Crystal Structures and Transition Sequences[J].J.Am.Ceram.Soc.,1998,81(8):1995-2012.
- [12] Chen J F,Guo F,Liang L,et al.Ultrafine Modified Aluminum Hydroxide and Its Preparation[P].US20050167641,2005-04-08.
- [13]汪忠清,梁顺琴,李斯琴.大孔容拟薄水铝石的研制及工业应用[J].石油化工,2001,30(3):220-223.
- [14]Munhoz A H,Mar tins J S,Ribeiro R R,et al.Use of Pseudo boehmite Nanoparticles for Drug Delivery System of Glucantime[J].J.Nano Res.,2016,38:47-51.
- [15]Panias D,Krestou A.Effect of Synthesis Parameters on Precipitation of Nanocrystalline Boehmite From Aluminate Solutions[J].Powder Technol.,2007,175:163-173.
- [16]Li Y,Zhang Y F,Chen F F,et al.Polymorphic Transformation of Aluminum Hydroxide Precipitated From Reactive NaAl(OH)_4-Na HCO_3 Solution[J].Cryst.Growth Des.,2011,11:1208-1214.
- [17]Katatny E A,Halawy S A,Mohamed M A,et al.A Novel Synthesis of High-Area Alumina Via H_2O_2-precipitated Boehmite From Sodium Alumina te Solution s[J].J.Chem.Technol.Biotechnol,1998,72:320-328.
- [18]杨清河,李大东,庄福成,等.NaAlO_2-CO_2法制备拟薄水铝石过程中的转化机理[J].催化学报,1997,18(6):478-482.
- [19]Zakharchenya R I,Vasilevskaya T N.Influence of Hydrolysis Temperature on the Hydrolysis Products of Aluminum Alkoxides[J].J.Mater.Sci.,1994,29:2806-2812.
- [20]Vaudry F,Khodabandeh S,Davis M E.Synthesis of Pure Alumina Mesoporous Materials[J].Chem.Mater.,1996,8:1451-1464.
- [21]周键儿,王艳香,马光华,等.溶胶-凝胶法制备超滤Al_2O_3膜的研究:Ⅰ勃姆石溶胶的制备[J].陶瓷学报,1999(2):87-91
- [22]Badkert P A,Bailey J E,Barker H A.Sintering and related phenomena[J].Mater.Sci.,Res.,1973,8(11):314-316.
- [23]Wang Y,Liu H T,Cheng H F,et al.Densification Behavior and Microstructure of Mullite Obtained from Diphasic Al_2O_3-SiO_2 Gels[J].Ceramics International,2014,40:12789-12796.
- [24] Ananthakumar S,Menon A R R.Prabhakaran K,et al.Rheology and Packing Characteristics of Alumina Extrusion Using Boehmite Gel As a Binder[J].Ceramics Interna tional,2001,27:231-237.
- [25]Ananthakumar S,Raja V,Warrier K G K.Effect of Nanoparticulate Boehmite Sol As a Dispersant For Slurry Compaction of Alumina Ceramics[J].Mater.Lett.,2000,43:174-179.
- [26]Yang R,Qi Z,Gao Y,et al.Effects of Alumina Sols on the Sintering of β-alumina Ceramics[J].Ceramics International,2020,46:20865-20870.